2.Mold polishing level

APG clamping machine with apg mold to casting epoxy resin products,APG insulator,APG bushing mold polishing level
A0=Ra0.08μm
A1=Ra0.016μm
A3=Ra0.0322
A4=Ra0.0632

P20 mold material treatment and advantages:
Hardened
In order to improve the life of the mold to more than 800,000 mold times, the pre-hardened steel can be quenched and low temperature return

The hard way of fire to achieve. When quenching, preheat at 500-600°C for 2-4 hours, then keep it at 850-880°C for a certain period of time (at least 2 hours), then put it in oil and cool to 50-100°C and air cooling. After quenching, the hardness can reach 50. -52HRC, in order to prevent cracking, 200℃ low temperature tempering treatment should be carried out immediately, after tempering, the hardness can be maintained above 48HRC

Nitriding treatment
Nitriding treatment can obtain high hardness surface structure, the surface hardness after nitriding reaches 650-700HV

(57-60HRC) The service life of the mold can reach more than 1 million times. The nitride layer has the characteristics of dense and smooth structure, and the mold release performance and resistance to humid air and alkali corrosion are improved.

Delivery status: The steel is delivered in annealed and hot rolled state.

Factory hardness: pre-hardened 29~33HRC

Material characteristics
● Uniform hardness, good polishing performance and photo-etching performance, good processing performance.

● Vacuum degassing and refining process pure steel, suitable for plastic molds that require polishing or etching. ● Supplied in a pre-hardened state, it can be directly used for mold processing without heat treatment, shortening the construction period.

● After forging and rolling, the structure is dense, 100% ultrasonic inspection, no pores, pinhole defects.